In superconductivity, a type-II superconductor is a superconductor that exhibits an intermediate phase of mixed ordinary and superconducting properties at intermediate temperature and fields above the superconducting phases.It also features the formation of magnetic field vortices with an applied external magnetic field.This occurs above a certain critical field strength Hc1. The vortex density increases with increasing field strength. At a higher critical field Hc2, superconductivity is destroyed. Type-II superconductors do not exhibit a complete Meissner effect.[1]
In 1935, J.N. Rjabinin and Lev Shubnikov[2] [3] experimentally discovered the type-II superconductors. In 1950, the theory of the two types of superconductors was further developed by Lev Landau and Vitaly Ginzburg in their paper on Ginzburg–Landau theory.[4] In their argument, a type-I superconductor had positive free energy of the superconductor-normal metal boundary. Ginzburg and Landau pointed out the possibility of type-II superconductors that should form inhomogeneous state in strong magnetic fields. However, at that time, all known superconductors were type-I, and they commented that there was no experimental motivation to consider precise structure of type-II superconducting state. The theory for the behavior of the type-II superconducting state in magnetic field was greatly improved by Alexei Alexeyevich Abrikosov,[5] who was elaborating on the ideas by Lars Onsager and Richard Feynman of quantum vortices in superfluids. Quantum vortex solution in a superconductor is also very closely related to Fritz London's work on magnetic flux quantization in superconductors. The Nobel Prize in Physics was awarded for the theory of type-II superconductivity in 2003.[6]
Ginzburg–Landau theory introduced the superconducting coherence length ξ in addition to London magnetic field penetration depth λ. According to Ginzburg–Landau theory, in a type-II superconductor
λ/\xi>1/\sqrt{2}
In 1952 an observation of type-II superconductivity was also reported by Zavaritskii. Fritz London demonstrated [7] [8] that a magnetic flux can penetrate a superconductor via a topological defect that has integer phase winding and carries quantized magnetic flux. Onsager and Feynman demonstrated that quantum vortices should form in superfluids.[9]
A 1957 paper by A. A. Abrikosov[10] generalizes these ideas. In the limit of very short coherence length the vortex solution is identical to London's fluxoid, where the vortex core is approximated by a sharp cutoff rather than a gradual vanishing of superconducting condensate near the vortex center. Abrikosov found that the vortices arrange themselves into a regular array known as a vortex lattice.[6] Near a so-called upper critical magnetic field, the problem of a superconductor in an external field is equivalent to the problem of vortex state in a rotating superfluid, discussed by Lars Onsager and Richard Feynman.
In the vortex state, a phenomenon known as flux pinning becomes possible. This is not possible with type-I superconductors, since they cannot be penetrated by magnetic fields.[11]
If a superconductor is cooled in a field, the field can be trapped, which can allow the superconductor to be suspended over a magnet, with the potential for a frictionless joint or bearing. The worth of flux pinning is seen through many implementations such as lifts, frictionless joints, and transportation. The thinner the superconducting layer, the stronger the pinning that occurs when exposed to magnetic fields.
Type-II superconductors are usually made of metal alloys or complex oxide ceramics. All high-temperature superconductors are type-II superconductors. While most elemental superconductors are type-I, niobium, vanadium, and technetium are elemental type-II superconductors. Boron-doped diamond and silicon are also type-II superconductors. Metal alloy superconductors can also exhibit type-II behavior (e.g., niobium–titanium, one of the most common superconductors in applied superconductivity), as well as intermetallic compounds like niobium–tin.
Other type-II examples are the cuprate-perovskite ceramic materials which have achieved the highest superconducting critical temperatures. These include La1.85Ba0.15CuO4, BSCCO, and YBCO (Yttrium-Barium-Copper-Oxide), which is famous as the first material to achieve superconductivity above the boiling point of liquid nitrogen (77 K). Due to strong vortex pinning, the cuprates are close to ideally hard superconductors.
Strong superconducting electromagnets (used in MRI scanners, NMR machines, and particle accelerators) often use coils wound of niobium-titanium wires or, for higher fields, niobium-tin wires. These materials are type-II superconductors with substantial upper critical field Hc2, and in contrast to, for example, the cuprate superconductors with even higher Hc2, they can be easily machined into wires. Recently, however, 2nd generation superconducting tapes are allowing replacement of cheaper niobium-based wires with much more expensive, but superconductive at much higher temperatures and magnetic fields "2nd generation" tapes.