A diffused junction transistor is a transistor formed by diffusing dopants into a semiconductor substrate. The diffusion process was developed later than the alloy-junction and grown junction processes for making bipolar junction transistors (BJTs).
Bell Labs developed the first prototype diffused junction bipolar transistors in 1954.[1]
The earliest diffused junction transistors were diffused-base transistors. These transistors still had alloy emitters and sometimes alloy collectors like the earlier alloy-junction transistors. Only the base was diffused into the substrate. Sometimes the substrate formed the collector, but in transistors like Philco's micro-alloy diffused transistors the substrate was the bulk of the base.
At Bell Labs Calvin Souther Fuller produced basic physical understanding of a means of directly forming the emitter, base, and collector by double diffusion. The method was summarized in a history of science at Bell:[2]
"Fuller had shown that acceptors of low atomic weight diffuse more rapidly than donors, which made possible n–p–n structures by simultaneous diffusion of donors and acceptors of appropriately different surface concentrations. The first n layer (the emitter) was formed because of the greater surface concentration of the donor (for example, antimony). The base formed beyond it because of the more rapid diffusion of the acceptor (for example, aluminum). The inner (collector) boundary of the base appeared where the diffused aluminum no longer over-compensated the n-type background doping of the original silicon. The base layers of the resulting transistors were 4 μm thick. ... Resulting transistors had a cut-off frequency of 120 MHz."
Texas Instruments made the first grown-junction silicon transistors in 1954.[3] The diffused silicon mesa transistor was developed at Bell Labs in 1955 and made commercially available by Fairchild Semiconductor in 1958.
These transistors were the first to have both diffused bases and diffused emitters. Unfortunately, like all earlier transistors, the edge of the collector–base junction was exposed, making it sensitive to leakage through surface contamination, thus requiring hermetic seals or passivation to prevent degradation of the transistor's characteristics over time.[4]
The planar transistor was developed by Dr. Jean Hoerni[5] at Fairchild Semiconductor in 1959. The planar process used to make these transistors made mass-produced monolithic integrated circuits possible.
Planar transistors have a silica passivation layer to protect the junction edges from contamination, making inexpensive plastic packaging possible without risking degradation of the transistor's characteristics over time.
The first planar transistors had a switching speed much lower than alloy junction transistors of the period, but as they could be mass-produced, and alloy junction transistors could not, they cost much less, and the characteristics of planar transistors improved very rapidly, quickly exceeding those of all earlier transistors and making earlier transistors obsolete.