Pauling's rules explained

Pauling's rules are five rules published by Linus Pauling in 1929 for predicting and rationalizing the crystal structures of ionic compounds.^{[1] [2]}

First rule: the radius ratio rule

See main article: Cation-anion radius ratio.

r _{+} / r _{-} (or r _{c} / r _{a} ) determines the coordination number (C.N.) of the cation, as well as the shape of the coordinated polyhedron of anions.^[3]

For the coordination numbers and corresponding polyhedra in the table below, Pauling mathematically derived the minimum radius ratio for which the cation is in contact with the given number of anions (considering the ions as rigid spheres). If the cation is smaller, it will not be in contact with the anions which results in instability leading to a lower coordination number.

Polyhedron and minimum radius ratio for each coordination number! C.N.!! Polyhedron !! Radius ratio

3		0.155
4		0.225
6	octahedron	0.414
7	capped octahedron	0.592
8	square antiprism (anticube)	0.645
8	cube	0.732
9	triaugmented triangular prism	0.732
12	cuboctahedron	1.00

The three diagrams at right correspond to octahedral coordination with a coordination number of six: four anions in the plane of the diagrams, and two (not shown) above and below this plane. The central diagram shows the minimal radius ratio. The cation and any two anions form a right triangle, with

2 r _{-} = \sqrt 2 (r _{-} + r _{+)} , or \sqrt 2 r _{-} = r _{-} + r _{+} . Then r _{+} = (\sqrt 2 - 1 )r _{-} = 0 . 414 r _{-} . Similar geometrical proofs yield the minimum radius ratios for the highly symmetrical cases C.N. = 3, 4 and 8.^[4]

For C.N. = 6 and a radius ratio greater than the minimum, the crystal is more stable since the cation is still in contact with six anions, but the anions are further from each other so that their mutual repulsion is reduced. An octahedron may then form with a radius ratio greater than or equal to 0.414, but as the ratio rises above 0.732, a cubic geometry becomes more stable. This explains why in NaCl with a radius ratio of 0.55 has octahedral coordination, whereas in CsCl with a radius ratio of 0.93 has cubic coordination.^[5]

If the radius ratio is less than the minimum, two anions will tend to depart and the remaining four will rearrange into a tetrahedral geometry where they are all in contact with the cation.

The radius ratio rules are a first approximation which have some success in predicting coordination numbers, but many exceptions do exist.^[3] In a set of over 5000 oxides, only 66% of coordination environments agree with Pauling's first rule. Oxides formed with alkali or alkali-earth metal cations that contain multiple cation coordinations are common deviations from this rule.^[6]

Second rule: the electrostatic valence rule

For a given cation, Pauling defined^[2] the electrostatic bond strength to each coordinated anion as

s = (z)/(\nu) , where z is the cation charge and ν is the cation coordination number. A stable ionic structure is arranged to preserve local electroneutrality, so that the sum of the strengths of the electrostatic bonds to an anion equals the charge on that anion.\xi = \sum _{i} s _{i} where \xi is the anion charge and the summation is over the adjacent cations. For simple solids, the s _{i} are equal for all cations coordinated to a given anion, so that the anion coordination number is the anion charge divided by each electrostatic bond strength. Some examples are given in the table.

Cations with oxide O^2− ion! Cation !! Radius ratio|| Cation C.N. || Electrostatic
bond strength || Anion C.N.|-| Li⁺ || 0.34||4|| 0.25||8|-| Mg²⁺ || 0.47||6||0.33||6|-| Sc³⁺ ||0.60|| 6||0.5||4|}

Pauling showed that this rule is useful in limiting the possible structures to consider for more complex crystals such as the aluminosilicate mineral orthoclase,, with three different cations. However, from data analysis of oxides from the Inorganic Crystal Structure Database (ICSD), the result showed that only 20% of all oxygen atoms matched with the prediction from second rule (using a cutoff of 0.01).

Third rule: sharing of polyhedron corners, edges and faces

The sharing of edges and particularly faces by two anion polyhedra decreases the stability of an ionic structure. Sharing of corners does not decrease stability as much, so (for example) octahedra may share corners with one another.

The decrease in stability is due to the fact that sharing edges and faces places cations in closer proximity to each other, so that cation-cation electrostatic repulsion is increased. The effect is largest for cations with high charge and low C.N. (especially when r+/r- approaches the lower limit of the polyhedral stability). Generally, smaller elements fulfill the rule better.

As one example, Pauling considered the three mineral forms of titanium dioxide, each with a coordination number of 6 for the cations. The most stable (and most abundant) form is rutile, in which the coordination octahedra are arranged so that each one shares only two edges (and no faces) with adjoining octahedra. The other two, less stable, forms are brookite and anatase, in which each octahedron shares three and four edges respectively with adjoining octahedra.

Fourth rule: crystals containing different cations

In a crystal containing different cations, those of high valency and small coordination number tend not to share polyhedron elements with one another. This rule tends to increase the distance between highly charged cations, so as to reduce the electrostatic repulsion between them.

One of Pauling's examples is olivine,, where M is a mixture of at some sites and at others. The structure contains distinct tetrahedra which do not share any oxygens (at corners, edges or faces) with each other. The lower-valence and cations are surrounded by polyhedra which do share oxygens.

Fifth rule: the rule of parsimony

The number of essentially different kinds of constituents in a crystal tends to be small. The repeating units will tend to be identical because each atom in the structure is most stable in a specific environment. There may be two or three types of polyhedra, such as tetrahedra or octahedra, but there will not be many different types.

Limitation

In a study of 5000 oxides, only 13% of them satisfy all of the last 4 rules, indicating limited universality of Pauling's rules.

See also

• Goldschmidt tolerance factor
• Octet rule

References

]

Notes and References

1. Pauling L . 1929. The principles determining the structure of complex ionic crystals . J. Am. Chem. Soc.. 51 . 4 . 1010–1026 . 10.1021/ja01379a006 . Pauling, Linus .
2. Book: Pauling, Linus . The nature of the chemical bond and the structure of molecules and crystals; an introduction to modern structural chemistry . registration . Cornell University Press . Ithaca (NY) . 1960 . 3rd . 543–562 . 0-8014-0333-2.
3. Book: Housecroft . Catherine E. . Sharpe . Alan G. . Inorganic chemistry . 2005 . Pearson Prentice Hall . Upper Saddle River, NJ . 9780130399137 . 145 . 2nd.
4. Toofan . Jahansooz . A Simple Expression between Critical Radius Ratio and Coordination Number . . February 1994 . 71 . 2 . 147 . 10.1021/ed071p147. Following the erratum, equations should read \alpha = \arcsin{(\tfrac{ 12- CN}{ 12 }) ^{\tfrac{1} { 2 }}} and R = (\tfrac{ 12 }{ 12- CN}) ^{\tfrac{1} { 2 }}{ -1 } , (where 2 \alpha = bond angle)
5. Book: Petrucci . Ralph H. . Harwood . William S. . Herring . F. Geoffrey . General chemistry: principles and modern applications . 2002 . Prentice Hall . Upper Saddle River, NJ . 0-13-014329-4 . 518 . 8th.
6. George . Janine . Waroquiers . David . Di Stefano . Davide . Petretto . Guido . Rignanese . Gian‐Marco . Hautier . Geoffroy . 2020-05-04 . The Limited Predictive Power of the Pauling Rules . Angewandte Chemie International Edition . en . 59 . 19 . 7569–7575 . 10.1002/anie.202000829 . 1433-7851 . 7217010 . 32065708.