High-entropy-alloy nanoparticles explained

High-entropy-alloy nanoparticles (HEA-NPs) are nanoparticles having five or more elements alloyed in a single-phase solid solution structure.[1] HEA-NPs possess a wide range of compositional library, distinct alloy mixing structure, and nanoscale size effect, giving them huge potential in catalysis, energy, environmental, and biomedical applications.

Enabling synthesis

HEA-NPs are a structural analog to bulk high-entropy alloys (HEAs),[2] [3] but synthesized at the nanoscale. The formation of HEAs typically requires high temperature for multi-element mixing; however, high temperature acts against nano-material synthesis due to high-temperature-induced structure aggregation and surface reconstruction.

In 2018, HEA-NPs were firstly synthesized by a carbothermal shock synthesis. (The material and technology are patented.[4] [5]) The carbothermal shock employs a rapid high-temperature heating (e.g. 2000 K, in 55 ms) to enable the non-equilibrium synthesis of HEA-NPs with uniform size and homogeneous mixing despite containing immiscible combinations. Although rapid quenching is desired to maintain the solid-solution state, too fast cooling rate can hinder structural ordering. Therefore, the cooling rate should be chosen carefully based on the temperature-time-transformation diagram.[6]

Another guide that can be used for the synthesis is the Ellingham diagram. Elements at the top of the diagram are easily reduced and tend to form HEA-NPs, while elements at the bottom of the diagram tend to form high-entropy oxide NPs.

Later, other similar non-equilibrium "shock" methods were also introduced to synthesize HEA-NPs and other types of high entropy nanostructures.[7] [8] [9] Recently, a low temperature synthesis through simultaneous multi-cation exchange (below 900 K) has been demonstrated for high-entropy metal sulfide NPs, which may be applied to metal selenides, tellurides, phosphides, and halides as well.[10]

In 2024 a study showed that induction plasma can be used as a one-step method that enables the continuous synthesis of HEA-NPs directly from elemental metal powders via in-flight alloying.[11]

Structural analysis

Due to the random distribution of elements in HEA-NPs, in addition to conventional characterization methods, other methods with higher resolution are needed for their structural analysis. To analyze the random mixing of multiple elements, atomic electron tomography can be used, which provides positional precision of 21 pm and identification of atoms by periods.[12] Furthermore, X-ray absorption spectroscopy can give information on local coordination environments, while extended X-ray absorption fine structure can be used to get coordination numbers and bond distances.[13] Combined with hard X-ray photoelectron spectroscopy or X-ray absorption near-edge structure, these analyses can be used to explore structure–property relationships in HEA-NPs. In addition, due to the immense number of possibilities of compositions and surfaces (i.e., terrace, edge, and corner) available for HEA-NPs, simulations such as density functional theory calculations are also popularly used for their analysis.[14]

Properties and applications

HEA-NPs have a large compositional library, which enables tunability in chemical composition, structure, and associated properties. In HEA-NPs, the same type of atoms can have different local density of states because their neighboring atom compositions can be different.[15] Such variations in local environment lead to diverse and tunable adsorption energy levels, which can be beneficial to satisfy the Sabatier principle especially for complex reactions.

In addition, owing to the high entropy structure, HEA-NPs typically show improved structural stability. One suggested mechanism for the enhanced structural stability is through prevention of phase separation due to lattice distortions from different sized elements acting as diffusion barriers.[16] With the above merits, HEA-NPs have been used as high-performance catalysts for both thermochemical and electrochemical reactions, such as ammonia oxidation, decomposition, and water splitting.[17] [18] [19] High throughput and data mining approaches are being implemented toward accelerated materials discovery in the multi-dimensional space of HEA-NPs.[20] [21]

See also

Notes and References

  1. Yao . Yonggang . Huang . Zhennan . Xie . Pengfei . Lacey . Steven D. . Jacob . Rohit Jiji . Xie . Hua . Chen . Fengjuan . Nie . Anmin . Pu . Tiancheng . Rehwoldt . Miles . Yu . Daiwei . 2018-03-30 . Carbothermal shock synthesis of high-entropy-alloy nanoparticles . Science . en . 359 . 6383 . 1489–1494 . 10.1126/science.aan5412 . 0036-8075 . 29599236 . 2018Sci...359.1489Y . free.
  2. Yeh . J.-W. . Chen . S.-K. . Lin . S.-J. . Gan . J.-Y. . Chin . T.-S. . Shun . T.-T. . Tsau . C.-H. . Chang . S.-Y. . 2004 . Nanostructured High-Entropy Alloys with Multiple Principal Elements: Novel Alloy Design Concepts and Outcomes . Advanced Engineering Materials . 6 . 5 . 299–303 . 10.1002/adem.200300567 . 137380231 . 1527-2648.
  3. Cantor . B. . Chang . I. T. H. . Knight . P. . Vincent . A. J. B. . 2004-07-01 . Microstructural development in equiatomic multicomponent alloys . Materials Science and Engineering: A . en . 375-377 . 213–218 . 10.1016/j.msea.2003.10.257 . 0921-5093.
  4. US . 2019161840 . Thermal shock synthesis of multielement nanoparticles . 2019-05-30 . Yao . Hu . Yonggang . Liangbing . University of Maryland.
  5. US . 2018369771 . Nanoparticles and Systems and Methods for Synthesizing Nanoparticles Through Thermal Shock . 2018-12-27 . Hu . Chen . Yao . Liangbing . Yanan . Yonggang . University of Maryland.
  6. Yao . Yonggang . Dong . Qi . Brozena . Alexandra . Luo . Jian . Miao . Jianwei . Chi . Miaofang . Wang . Chao . Kevrekidis . Ioannis G. . Ren . Zhiyong Jason . Greeley . Jeffrey . Wang . Guofeng . Anapolsky . Abraham . Hu . Liangbing . 2022-04-08 . High-entropy nanoparticles: Synthesis-structure-property relationships and data-driven discovery . Science . en . 376 . 6589 . eabn3103 . 10.1126/science.abn3103 . 35389801 . 248024069 . 0036-8075.
  7. Yang . Yong . Song . Boao . Ke . Xiang . Xu . Feiyu . Bozhilov . Krassimir N. . Hu . Liangbing . Shahbazian-Yassar . Reza . Zachariah . Michael R. . 2020-03-03 . Aerosol Synthesis of High Entropy Alloy Nanoparticles . Langmuir . 36 . 8 . 1985–1992 . 10.1021/acs.langmuir.9b03392 . 32045255 . 211087047 . 0743-7463.
  8. Glasscott . Matthew W. . Pendergast . Andrew D. . Goines . Sondrica . Bishop . Anthony R. . Hoang . Andy T. . Renault . Christophe . Dick . Jeffrey E. . 2019-06-14 . Electrosynthesis of high-entropy metallic glass nanoparticles for designer, multi-functional electrocatalysis . Nature Communications . en . 10 . 1 . 2650 . 10.1038/s41467-019-10303-z . 31201304 . 6570760 . 2019NatCo..10.2650G . 2041-1723 . free.
  9. Chen . Hao . Lin . Wenwen . Zhang . Zihao . Jie . Kecheng . Mullins . David R. . Sang . Xiahan . Yang . Shi-Ze . Jafta . Charl J. . Bridges . Craig A. . Hu . Xiaobing . Unocic . Raymond R. . 2019-07-01 . Mechanochemical Synthesis of High Entropy Oxide Materials under Ambient Conditions: Dispersion of Catalysts via Entropy Maximization . ACS Materials Letters . 1 . 1 . 83–88 . 10.1021/acsmaterialslett.9b00064 . 181600242.
  10. McCormick . Connor R. . Schaak . Raymond E. . 2021-01-20 . Simultaneous Multication Exchange Pathway to High-Entropy Metal Sulfide Nanoparticles . Journal of the American Chemical Society . en . 143 . 2 . 1017–1023 . 10.1021/jacs.0c11384 . 33405919 . 230810629 . 0002-7863.
  11. Kim . Keun Su . Couillard . Martin . Tang . Ziqi . Shin . Homin . Poitras . Daniel . Cheng . Changjun . Naboka . Olga . Ruth . Dean . Plunkett . Mark . Chen . Lixin . Gaburici . Liliana . Lacelle . Thomas . Nganbe . Michel . Zou . Yu . 2024-02-16 . Continuous synthesis of high-entropy alloy nanoparticles by in-flight alloying of elemental metals . Nature Communications . en . 15 . 1 . 1450 . 10.1038/s41467-024-45731-z . 2041-1723 . 10873330 . 38365786. 2024NatCo..15.1450K .
  12. Yang . Yao . Zhou . Jihan . Zhu . Fan . Yuan . Yakun . Chang . Dillan J. . Kim . Dennis S. . Pham . Minh . Rana . Arjun . Tian . Xuezeng . Yao . Yonggang . Osher . Stanley J. . Schmid . Andreas K. . Hu . Liangbing . Ercius . Peter . Miao . Jianwei . April 2021 . Determining the three-dimensional atomic structure of an amorphous solid . Nature . en . 592 . 7852 . 60–64 . 10.1038/s41586-021-03354-0 . 33790443 . 2004.02266 . 2021Natur.592...60Y . 214802235 . 1476-4687.
  13. Morris . David . Yao . Yonggang . Finfrock . Y. Zou . Huang . Zhennan . Shahbazian-Yassar . Reza . Hu . Liangbing . Zhang . Peng . 2021-11-17 . Composition-dependent structure and properties of 5- and 15-element high-entropy alloy nanoparticles . Cell Reports Physical Science . en . 2 . 11 . 100641 . 10.1016/j.xcrp.2021.100641 . 2021CRPS....200641M . 243775798 . 2666-3864. free .
  14. Lu . Zhuole . Chen . Zhi Wen . Singh . Chandra Veer . 2020-10-07 . Neural Network-Assisted Development of High-Entropy Alloy Catalysts: Decoupling Ligand and Coordination Effects . Matter . English . 3 . 4 . 1318–1333 . 10.1016/j.matt.2020.07.029 . 2590-2393. free .
  15. Wu . Dongshuang . Kusada . Kohei . Nanba . Yusuke . Koyama . Michihisa . Yamamoto . Tomokazu . Toriyama . Takaaki . Matsumura . Syo . Seo . Okkyun . Gueye . Ibrahima . Kim . Jaemyung . Rosantha Kumara . Loku Singgapulige . Sakata . Osami . Kawaguchi . Shogo . Kubota . Yoshiki . Kitagawa . Hiroshi . 2022-03-02 . Noble-Metal High-Entropy-Alloy Nanoparticles: Atomic-Level Insight into the Electronic Structure . Journal of the American Chemical Society . en . 144 . 8 . 3365–3369 . 10.1021/jacs.1c13616 . 35166532 . 0002-7863.
  16. Kube . Sebastian A. . Schroers . Jan . 2020-09-01 . Metastability in high entropy alloys . Scripta Materialia . en . 186 . 392–400 . 10.1016/j.scriptamat.2020.05.049 . 225335588 . 1359-6462. free .
  17. Xie . Pengfei . Yao . Yonggang . Huang . Zhennan . Liu . Zhenyu . Zhang . Junlei . Li . Tangyuan . Wang . Guofeng . Shahbazian-Yassar . Reza . Hu . Liangbing . Wang . Chao . 2019-09-05 . Highly efficient decomposition of ammonia using high-entropy alloy catalysts . Nature Communications . en . 10 . 1 . 4011 . 10.1038/s41467-019-11848-9 . 31488814 . 6728353 . 2019NatCo..10.4011X . 2041-1723 . free.
  18. Yang . Chunpeng . Yao . Yonggang . He . Shuaiming . Xie . Hua . Hitz . Emily . Hu . Liangbing . 2017 . Ultrafine Silver Nanoparticles for Seeded Lithium Deposition toward Stable Lithium Metal Anode . Advanced Materials . en . 29 . 38 . 1702714 . 10.1002/adma.201702714 . 28833607 . 2017AdM....2902714Y . 205281575 . 1521-4095.
  19. Gao . Shaojie . Hao . Shaoyun . Huang . Zhennan . Yuan . Yifei . Han . Song . Lei . Lecheng . Zhang . Xingwang . Shahbazian-Yassar . Reza . Lu . Jun . 2020-04-24 . Synthesis of high-entropy alloy nanoparticles on supports by the fast moving bed pyrolysis . Nature Communications . 11 . 1 . 2016 . 10.1038/s41467-020-15934-1 . 32332743 . 7181682 . 2020NatCo..11.2016G . 2041-1723 . free.
  20. Yao . Yonggang . Liu . Zhenyu . Xie . Pengfei . Huang . Zhennan . Li . Tangyuan . Morris . David . Finfrock . Zou . Zhou . Jihan . Jiao . Miaolun . Gao . Jinlong . Mao . Yimin . 2020 . Computationally aided, entropy-driven synthesis of highly efficient and durable multi-elemental alloy catalysts . Science Advances . 6 . 11 . eaaz0510 . 10.1126/sciadv.aaz0510 . 32201728 . 7069714 . 2020SciA....6..510Y . 2375-2548 . free.
  21. Yao . Yonggang . Huang . Zhennan . Li . Tangyuan . Wang . Hang . Liu . Yifan . Stein . Helge S. . Mao . Yimin . Gao . Jinlong . Jiao . Miaolun . Dong . Qi . Dai . Jiaqi . 2020-03-24 . High-throughput, combinatorial synthesis of multimetallic nanoclusters . Proceedings of the National Academy of Sciences . en . 117 . 12 . 6316–6322 . 10.1073/pnas.1903721117 . 0027-8424 . 32156723 . 7104385 . 2020PNAS..117.6316Y . free.

This article is licensed under the GNU Free Documentation License. It uses material from the Wikipedia article "High-entropy-alloy nanoparticles".

Except where otherwise indicated, Everything.Explained.Today is © Copyright 2009-2024, A B Cryer, All Rights Reserved. Cookie policy.