The Faber–Evans model for crack deflection,[1] [2] is a fracture mechanics-based approach to predict the increase in toughness in two-phase ceramic materials due to crack deflection.[3] The effect is named after Katherine Faber and her mentor, Anthony G. Evans, who introduced the model in 1983.[4] The Faber–Evans model is a principal strategy for tempering brittleness and creating effective ductility.[5]
Fracture toughness is a critical property of ceramic materials, determining their ability to resist crack propagation and failure.[6] The Faber model considers the effects of different particle morphologies, including spherical, rod-shaped, and disc-shaped particles, and their influence on the driving force at the tip of a tilted and/or twisted crack. The model first suggested that rod-shaped particles with high aspect ratios are the most effective morphology for deflecting propagating cracks and increasing fracture toughness, primarily due to the twist of the crack front between particles. The findings provide a basis for designing high-toughness two-phase ceramic materials, with a focus on optimizing particle shape and volume fraction.
Fracture mechanics is a fundamental discipline for understanding the mechanical behavior of materials, particularly in the presence of cracks. The critical parameter in fracture mechanics is the stress intensity factor (K), which is related to the strain energy release rate (G) and the fracture toughness (Gc). When the stress intensity factor reaches the material's fracture toughness, crack propagation becomes unstable, leading to failure.
In two-phase ceramic materials, the presence of a secondary phase can lead to crack deflection, a phenomenon where the crack path deviates from its original direction due to interactions with the second-phase particles.[7] Crack deflection can lead to a reduction in the driving force at the crack tip, increasing the material's fracture toughness. The effectiveness of crack deflection in enhancing fracture toughness depends on several factors, including particle shape, size, volume fraction, and spatial distribution.
The study presents weighting functions, F(θ), for the three particle morphologies, which describe the distribution of tilt angles (θ) along the crack front:
F(\theta)\rm=\left(
4 | |
\pi |
\right)\sin2\thetad\theta
F(\theta)\rm=\left(
4 | |
\pi |
\right)\sin2\thetad\theta
F(\theta)\rm ≈ (1.55+1.10\theta-2.42\theta2+1.78\theta3)sin\thetacos\thetad\theta
The weighting functions are used to determine the net driving force on the tilted crack for each morphology. The relative driving force for spherical particles is given by:
\left\langle{G}\right
t/G | |
\rangle | |
infty=\left |
(
4 | |
\pi |
\right
t) | |
)\sin | |
1 |
t)]d\theta | |
2 |
where
ki=ki/K1
\left\langle{G}\right\ranglet
\left\langle{G}\right\ranglet
t | |
(G | |
\rmc |
)sphere=(1+0.87Vf)G
m | |
\rmc |
t | |
(G | |
\rmc |
)rod
m | |
≈ (1+V | |
\rmc |
t | |
(G | |
\rmc |
)disk=[1+0.56Vf(r/t)]G
m | |
\rmc |
where represents the fracture toughness of the matrix material without the presence of any reinforcing particles,
Vf
(H/r)
H
r
(r/t)
r
t
The spatial location and orientation of adjacent particles play a crucial role in determining whether the inter-particle crack front will tilt or twist. If adjacent particles produce tilt angles of opposite sign, twist of the crack front will result. Conversely, tilt angles of like sign at adjacent particles cause the entire crack front to tilt. Therefore, to evaluate the toughening increment, all possible particle configurations must be considered.
For spherical particles, the average twist angle is determined by the mean center-to-center nearest neighboring distance,
\Delta
\Delta | = | |
r |
| ||||||
|
infty | |
\int | |
8Vf |
x1/3e-xdx
The maximum twist angle occurs when the particles are nearly co-planar with the crack, given by:
\phimax=\sin-1\left(
2r | |
\Delta |
\right)
and depends exclusively on the volume fraction.
For rod-shaped particles, the analysis of crack front twist is more complex due to difficulties in describing the rod orientation with respect to the crack front and adjacent rods. The twist angle,
\phi
λ
\phi=\tan-1\left\{
\alpha\sin\theta1+(1-\beta)\sin\theta2 | |
\Delta' |
\right\}
where
\Delta'
The analysis reveals that rod-shaped particles with high aspect ratios are the most effective morphology for deflecting propagating cracks, with the potential to increase fracture toughness by up to four times. This toughening arises primarily from the twist of the crack front between particles. Disc-shaped particles and spheres are less effective in increasing fracture toughness.
For disc-shaped particles with high aspect ratios, initial crack front tilt can provide significant toughening, although the twist component still dominates. In contrast, neither sphere nor rod particles derive substantial toughening from the initial tilting process. As the volume fraction of particles increases, an asymptotic toughening effect is observed for all three morphologies at volume fractions above 0.2. For spherical particles, the interparticle spacing distribution has a significant impact on toughening, with greater enhancements when spheres are nearly contacting and twist angles approach π/2.
The Faber–Evans model suggests that rod-shaped particles with high aspect ratios are the most effective morphology for deflecting propagating cracks and increasing fracture toughness, primarily due to the twist of the crack front between particles. Disc-shaped particles and spheres are less effective in enhancing toughness. However, the interparticle spacing distribution plays a significant role in the toughening by spherical particles, with greater toughening achieved when spheres are nearly contacting.
In designing high-toughness two-phase ceramic materials, the focus should be on optimizing particle shape and volume fraction. The model proved that ideal second phase should be chemically compatible and present in amounts of 10 to 20 volume percent, with particles having high aspect ratios, particularly those with rod-shaped morphologies, providing the maximum toughening effect.[9] This model is often used in the development of advanced ceramic materials with improved performance when the factors that contribute to the increase in fracture toughness is a consideration.[10] [11]