475 °C embrittlement explained

Duplex stainless steels are a family of alloys with a two-phase microstructure consisting of both austenitic (face-centred cubic) and ferritic (body-centred cubic) phases. They offer excellent mechanical properties, corrosion resistance, and toughness compared to other types of stainless steel. However, duplex stainless steel can be susceptible to a phenomenon known as 475C embrittlement or duplex stainless steel age hardening, which is a type of aging process that causes loss of plasticity in duplex stainless steel when it is heated in the range of 250C550C. At this temperature range, spontaneous phase separation of the ferrite phase into iron-rich and chromium-rich nanophases occurs, with no change in the mechanical properties of the austenite phase. This type of embrittlement is due to precipitation hardening, which makes the material become brittle and prone to cracking.

Duplex stainless steel

See also: Duplex stainless steel. Duplex stainless steel is a type of stainless steel that has a two-phase microstructure consisting of both austenitic (face-centred cubic) and ferritic (body-centred cubic) phases. This dual-phase structure gives duplex stainless steel a combination of mechanical and corrosion-resistant properties that are superior to those of either austenitic or ferritic stainless steel alone. The austenitic phase provides the steel with good ductility, high toughness, and high corrosion resistance, especially in acidic and chloride-containing environments. The ferritic phase, on the other hand, provides the steel with good strength, high resistance to stress corrosion cracking, and high resistance to pitting and crevice corrosion. They are therefore used extensively in the offshore oil and gas industry for pipework systems, manifolds, risers, etc. and in the petrochemical industry in the form of pipelines and pressure vessels.[1]

A duplex stainless steel mixture of austenite and ferrite microstructure is not necessarily in equal proportions, and where the alloy solidifies as ferrite, it is partially transformed to austenite when the temperature falls to around . Duplex steels have a higher chromium content compared to austenitic stainless steel, 20–28%; higher molybdenum, up to 5%; lower nickel, up to 9%; and 0.05–0.50% nitrogen.[2] [3] Thus, duplex stainless steel alloys have good corrosion resistance and higher strength than standard austenitic stainless steels such as type 304 or 316.[4] [5]

Alpha (α) phase is a ferritic phase with body-centred cubic (BCC) structure, Im

\bar{3}

m [229] space group, 2.866 Å lattice parameter, and has one twinning system <111> and three slip systems <111>, <111> and <111>; however, the last system rarely activates.[6] [7] Gamma (

\gamma

) phase is austenitic with a face-centred cubic (FCC) structure, Fm

\bar{3}

m [259] space group, and 3.66 Å lattice parameter. It normally has more nickel, copper, and interstitial carbon and nitrogen.[8] Plastic deformation occurs in austenite more readily than in ferrite.[9] [10] During deformation, straight slip bands form in the austenite grains and propagate to the ferrite-austenite grain boundaries, assisting in the slipping of the ferrite phase. Curved slip bands also form due to the bulk-ferrite-grain deformation.[11] [12] [13] The formation of slip bands indicates a concentrated unidirectional slip on certain planes causing a stress concentration.[14]

Age hardening by spinodal decomposition

See also: Spinodal decomposition.

Duplex stainless steel can have limited toughness due to its large ferritic grain size, and its tendencies to hardening and embrittlement, i.e., loss of plasticity, at temperatures ranging from 250C550C, especially at . At this temperature range, spinodal decomposition of the supersaturated solid ferrite solution into iron-rich nanophase (

\acute{a}

) and chromium-rich nanophase (

\acute{a}\acute{}

), accompanied by G-phase precipitation, occurs.[15] [16] [17] This makes the ferrite phase a preferential initiation site for micro-cracks.[18] This is because aging encourages Σ3 <111> ferrite deformation twinning at slow strain rate and room temperature in tensile or compressive deformation, nucleating from local stress concentration sites,[19] and parent-twinning boundaries, with 60° (in or out) misorientation, are suitable for cleavage crack nucleation.[20] [21]

Spinodal decomposition refers to the spontaneous separation of a phase into two coherent phases via uphill diffusion, i.e., from a region of lower concentration to a region of higher concentration resulting in a negative diffusion coefficient

{d2G\overdx2}

, without a barrier to nucleation due to the phase being thermodynamically unstable (i.e., miscibility gap,

\acute{a}

+

\acute{a}\acute{}

region in the figure),[22] where

G

is the Gibbs free energy per mole of solution and the composition. It increases hardness and decreases magneticity.[23] Miscibility gap describes the region in a phase diagram below the melting point of each compound where the solid phase splits into the liquid of two separated stable phases.[24]

For 475 °C embrittlement to occur, the chromium content needs to exceed 12%.[25] The addition of nickel accelerates the spinodal decomposition by promoting the iron-rich nanophase formation.[26] Nitrogen changes the distribution of chromium, nickel, and molybdenum in the ferrite phase but does not prevent the phase decomposition.[27] Other elements like molybdenum, manganese, and silicon do not affect the formation of iron-rich nanophase.[28] However, manganese and molybdenum partition to the iron-rich nanophase, while nickel partitions to the chromium-rich nanophase.

Microscopy characterisation

Using Field Emission Gun Transmission Electron Microscope FEG-TEM, the nanometre-scaled modulated structure of the decomposed ferrite was revealed as chromium-rich nanophase gave the bright image, and iron-rich darker image. It also revealed that these modulated nanophases grow coarser with aging time.[29] Decomposed phases start as irregular rounded shapes with no particular arrangement, but with time the chromium-rich nanophase takes a plat shape aligned in the <110> directions.

Consequences

Spinodal decomposition increases the hardening of the material due to the misfit between the chromium-rich and iron-rich nano-phases, internal stress, and variation of elastic modulus. The formation of coherent precipitates induces an equal but opposite strain, raising the system's free energy depending on the precipitate shape and matrix and precipitate elastic properties.[30] Around a spherical inclusion, the distortion is purely hydrostatic.

G-phase precipitates appear prominently at grain boundaries. and are phase rich in nickel, titanium, and silicon, but chromium and manganese may substitute titanium sites.[31] G-phase precipitates occur during long-term aging, are encouraged by increasing nickel content in the ferrite phase, and reduce corrosion resistance significantly.[32] It has ellipsoid morphology, structure (Fm

\bar{3}

m), and 11.4 Å lattice parameter,[33] with a diameter less than 50 nm that increases with aging.[34] [35]

Thus, the embrittlement is caused by dislocations impediment/ locking by the spinodally decomposed matrix[36] [37] and strain around G-phase precipitates,[38] i.e., internal stress relaxation by the formation of Cottrell atmosphere.[39]

Furthermore, the ferrite hardness increases with aging time, the hardness of the ductile austenite phase remains nearly unchanged[40] due to faster diffusivity in ferrite compared to the austenite. However, austenite undergoes a substitutional redistribution of elements, enhancing galvanic corrosion between the two phases.[41]

Treatment

550 °C heat treatment can reverse spinodal decomposition but not affect the G-phase precipitates.[42] The ferrite matrix spinodal decomposition can be substantially reversed by introducing an external pulsed electric current that changes the system's free energy due to the difference in electrical conductivity between the nanophases and the dissolution of G-phase precipitates.[43] [44] Cyclic loading suppresses spinodal decomposition,[45] and radiation accelerates it but changes the decomposition nature from an interconnected network of modulated nanophases to isolated islands.[46]

Further reading

Notes and References

  1. Web site: International Stainless Steel Forum . 2020 . Duplex Stainless Steels . 2023-03-25 . 2023-03-05 . https://web.archive.org/web/20230305111743/https://www.worldstainless.org/Files/issf/non-image-files/PDF/ISSF_Duplex_Stainless_Steels.pdf . live .
  2. Book: International Molybdenum Association (IMOA) . Practical Guidelines for the Fabrication of Duplex Stainless Steels . 3rd . 2014 . 978-1-907470-09-7 . 2023-03-25 . 2023-03-10 . https://web.archive.org/web/20230310023353/https://www.imoa.info/download_files/stainless-steel/Duplex_Stainless_Steel_3rd_Edition.pdf . live .
  3. Book: Charles, Jacques . Proceedings of the Duplex Stainless Steel Conference, Beaune (2010) . EDP Sciences, Paris . 2010 . 29–82 . 2023-03-25 . 2022-05-06 . https://web.archive.org/web/20220506081328/https://pubs.kci-webshop.com/Webshop/Product/BOOKS/Duplex-Stainless-Steel---DSS-2010-Conference-Proceedings.html . live .
  4. Alvarez-Armas . Iris . Duplex Stainless Steels: Brief History and Some Recent Alloys . Recent Patents on Mechanical Engineering . 2008 . en . 1 . 1 . 51–57 . 10.2174/2212797610801010051 . 2022-10-14 . 2022-10-14 . https://web.archive.org/web/20221014000404/https://www.eurekaselect.com/article/40020 . live .
  5. Book: Peckner . Donald . Handbook of Stainless Steels . Bernstein . I.M. . McGraw Hill . 1977 . 9780070491472 . chapter 8.
  6. Du . C. . Maresca . F. . Geers . M. G. D. . Hoefnagels . J. P. M. . 2018-03-01 . Ferrite slip system activation investigated by uniaxial micro-tensile tests and simulations . Acta Materialia . en . 146 . 314–327 . 10.1016/j.actamat.2017.12.054 . 2018AcMat.146..314D . 1359-6454.
  7. Koko . Abdalrhaman . Elmukashfi . Elsiddig . Dragnevski . Kalin . Wilkinson . Angus J. . Marrow . Thomas James . 2021-10-01 . J-integral analysis of the elastic strain fields of ferrite deformation twins using electron backscatter diffraction . Acta Materialia . en . 218 . 117203 . 10.1016/j.actamat.2021.117203 . 2021AcMat.21817203K . 1359-6454.
  8. Nilsson . J.-O. . 1992-08-01 . Super duplex stainless steels . Materials Science and Technology . 8 . 8 . 685–700 . 10.1179/mst.1992.8.8.685 . 1992MatST...8..685N . 0267-0836 . 2022-10-14 . 2023-03-25 . https://web.archive.org/web/20230325224755/https://www.tandfonline.com/doi/abs/10.1179/mst.1992.8.8.685 . live .
  9. Zieliński . W. . Świątnicki . W. . Barstch . M. . Messerschmidt . U. . 2003-08-28 . Non-uniform distribution of plastic strain in duplex steel during TEM in situ deformation . Materials Chemistry and Physics . en . 81 . 2 . 476–479 . 10.1016/S0254-0584(03)00059-2 . 0254-0584.
  10. Koko . Abdalrhaman . Elmukashfi . Elsiddig . Becker . Thorsten H. . Karamched . Phani S. . Wilkinson . Angus J. . Marrow . T. James . 2022-10-15 . In situ characterisation of the strain fields of intragranular slip bands in ferrite by high-resolution electron backscatter diffraction . Acta Materialia . en . 239 . 118284 . 10.1016/j.actamat.2022.118284 . 2022AcMat.23918284K . 251783802 . 1359-6454. free .
  11. Serre . I. . Salazar . D. . Vogt . J.-B. . September 2008 . Atomic force microscopy investigation of surface relief in individual phases of deformed duplex stainless steel . Materials Science and Engineering: A . en . 492 . 1–2 . 428–433 . 10.1016/j.msea.2008.04.060 . 2022-10-14 . 2022-08-11 . https://web.archive.org/web/20220811205256/https://linkinghub.elsevier.com/retrieve/pii/S0921509308005157 . live .
  12. Li Z, Hu Y, Chen T, Wang X, Liu P, Lu Y . Microstructural Evolution and Mechanical Behavior of Thermally Aged Cast Duplex Stainless Steel . Materials . 13 . 24 . 5636 . December 2020 . 33321825 . 7763132 . 10.3390/ma13245636 . 2020Mate...13.5636L . free .
  13. Zhang . Qingdong . Ma . Sida . Jing . Tao . March 2019 . Mechanical Properties of a Thermally-aged Cast Duplex Stainless Steel by in Situ Tensile Test at the Service Temperature . Metals . en . 9 . 3 . 317 . 10.3390/met9030317 . 2075-4701. free .
  14. Sangid . Michael D. . 2013-12-01 . The physics of fatigue crack initiation . International Journal of Fatigue . Fatigue and Microstructure: A special issue on recent advances . en . 57 . 58–72 . 10.1016/j.ijfatigue.2012.10.009 . 0142-1123.
  15. Örnek . Cem . Burke . M. G. . Hashimoto . T. . Engelberg . D. L. . April 2017 . 748 K (475 °C) Embrittlement of Duplex Stainless Steel: Effect on Microstructure and Fracture Behavior . Metallurgical and Materials Transactions A . en . 48 . 4 . 1653–1665 . 10.1007/s11661-016-3944-2 . 2017MMTA...48.1653O . 136321604 . 1073-5623. free .
  16. Weng . K. L . Chen . H. R . Yang . J. R . 2004-08-15 . The low-temperature aging embrittlement in a 2205 duplex stainless steel . Materials Science and Engineering: A . en . 379 . 1 . 119–132 . 10.1016/j.msea.2003.12.051 . 0921-5093.
  17. Beattie . H. J. . Versnyder . F. L. . July 1956 . A New Complex Phase in a High-Temperature Alloy . Nature . en . 178 . 4526 . 208–209 . 10.1038/178208b0 . 1956Natur.178..208B . 4217639 . 1476-4687 . 2022-10-14 . 2022-10-14 . https://web.archive.org/web/20221014102507/https://www.nature.com/articles/178208b0 . live .
  18. Liu . Gang . Li . Shi-Lei . Zhang . Hai-Long . Wang . Xi-Tao . Wang . Yan-Li . August 2018 . Characterization of Impact Deformation Behavior of a Thermally Aged Duplex Stainless Steel by EBSD . Acta Metallurgica Sinica (English Letters) . en . 31 . 8 . 798–806 . 10.1007/s40195-018-0708-6 . 139395583 . 1006-7191. free .
  19. Marrow . T. J. . Humphreys . A. O. . Strangwood . M. . The Crack Initiation Toughness for Brittle Fracture of Super Duplex Stainless Steel . July 1997 . Fatigue & Fracture of Engineering Materials & Structures . en . 20 . 7 . 1005–1014 . 10.1111/j.1460-2695.1997.tb01543.x . 2022-10-14 . 2022-10-14 . https://web.archive.org/web/20221014000357/https://onlinelibrary.wiley.com/doi/10.1111/j.1460-2695.1997.tb01543.x . live .
  20. Kato . Masaharu . January 1981 . Hardening by spinodally modulated structure in b.c.c. alloys . Acta Metallurgica . en . 29 . 1 . 79–87 . 10.1016/0001-6160(81)90088-2 . 2022-10-14 . 2018-07-03 . https://web.archive.org/web/20180703104514/https://linkinghub.elsevier.com/retrieve/pii/0001616081900882 . live .
  21. Marrow . T. J. . Harris . C. . July 1996 . The Fracture Mechanism of 475°C Embrittlement in a Duplex Stainless Steel . Fatigue & Fracture of Engineering Materials & Structures . en . 19 . 7 . 935–947 . 10.1111/j.1460-2695.1996.tb01028.x . 2022-10-14 . 2022-10-14 . https://web.archive.org/web/20221014000356/https://onlinelibrary.wiley.com/doi/10.1111/j.1460-2695.1996.tb01028.x . live .
  22. Mburu . Sarah . Kolli . R. Prakash . Perea . Daniel E. . Schwarm . Samuel C. . Eaton . Arielle . Liu . Jia . Patel . Shiv . Bartrand . Jonah . Ankem . Sreeramamurthy . April 2017 . Effect of aging temperature on phase decomposition and mechanical properties in cast duplex stainless steels . Materials Science and Engineering: A . en . 690 . 365–377 . 10.1016/j.msea.2017.03.011. free .
  23. Örnek . C. . Burke . M. G. . Hashimoto . T. . Lim . J. J. H. . Engelberg . D. L. . 2017-05-26 . 475°C Embrittlement of Duplex Stainless Steel—A Comprehensive Microstructure Characterization Study . Materials Performance and Characterization . en . 6 . 3 . MPC20160088 . 10.1520/MPC20160088 . 2022-10-14 . 2018-06-03 . https://web.archive.org/web/20180603060647/https://www.astm.org/doiLink.cgi?MPC20160088 . live .
  24. Book: Porter . David A. . Easterling . Kenneth E. . Sherif . Mohamed Y. . Phase Transformations in Metals and Alloys . 2021 . CRC Press . 978-1-000-46779-6 . [S.l.] . 1267751972.
  25. Sahu . J. K. . Krupp . U. . Ghosh . R. N. . Christ . H. -J. . 2009-05-20 . Effect of 475°C embrittlement on the mechanical properties of duplex stainless steel . Materials Science and Engineering: A . en . 508 . 1 . 1–14 . 10.1016/j.msea.2009.01.039 . 0921-5093.
  26. Miller . M. K. . Russell . K. F. . 1996-03-02 . Comparison of the rate of decomposition in Fe-45%Cr,Fe-45%Cr-5%Ni and duplex stainless steels . Applied Surface Science . Proceedings of the 42nd International Field Emission Symposium . en . 94-95 . 398–402 . 10.1016/0169-4332(95)00403-3 . 1996ApSS...94..398M . 0169-4332.
  27. Bliznuk . T. . Mola . M. . Polshin . E. . Pohl . M. . Gavriljuk . V. . 2005-09-25 . Effect of nitrogen on short-range atomic order in the feritic δ phase of a duplex steel . Materials Science and Engineering: A . en . 405 . 1 . 11–17 . 10.1016/j.msea.2005.05.094 . 0921-5093.
  28. Solomon . H. D. . Levinson . Lionel M. . 1978-03-01 . Mössbauer effect study of '475°c embrittlement' of duplex and ferritic stainless steels . Acta Metallurgica . en . 26 . 3 . 429–442 . 10.1016/0001-6160(78)90169-4 . 0001-6160.
  29. Soriano-Vargas . Orlando . Avila-Davila . Erika O. . Lopez-Hirata . Victor M. . Cayetano-Castro . Nicolas . Gonzalez-Velazquez . Jorge L. . May 2010 . Effect of spinodal decomposition on the mechanical behavior of Fe–Cr alloys . Materials Science and Engineering: A . en . 527 . 12 . 2910–2914 . 10.1016/j.msea.2010.01.020 . 2022-10-14 . 2022-08-03 . https://web.archive.org/web/20220803091909/https://linkinghub.elsevier.com/retrieve/pii/S0921509310000353 . live .
  30. Cahn . John W . 1961-09-01 . On spinodal decomposition . Acta Metallurgica . en . 9 . 9 . 795–801 . 10.1016/0001-6160(61)90182-1 . 0001-6160 . 2022-10-14 . 2023-03-25 . https://web.archive.org/web/20230325224817/https://www.sciencedirect.com/science/article/abs/pii/0001616061901821?via%3Dihub . live .
  31. Sakata . Mikihiro . Kadoi . Kota . Inoue . Hiroshige . December 2021 . Acceleration of 475 °C embrittlement in weld metal of 22 mass% Cr-duplex stainless steel . Materials Today Communications . en . 29 . 102800 . 10.1016/j.mtcomm.2021.102800. 240575697 . free .
  32. Xue . Fei . Shi . Fangjie . Zhang . Chuangju . Zheng . Qiaoling . Yi . Dawei . Li . Xiuqing . Li . Yefei . 2021-07-21 . The Microstructure and Mechanical and Corrosion Behaviors of Thermally Aged Z3CN20-09M Cast Stainless Steel for Primary Coolant Pipes of Nuclear Power Plants . Coatings . en . 11 . 8 . 870 . 10.3390/coatings11080870 . 2079-6412. free .
  33. Li . Shilei . Wang . Yanli . Wang . Xitao . Xue . Fei . September 2014 . G-phase precipitation in duplex stainless steels after long-term thermal aging: A high-resolution transmission electron microscopy study . Journal of Nuclear Materials . en . 452 . 1–3 . 382–388 . 10.1016/j.jnucmat.2014.05.069 . 2014JNuM..452..382L . 2022-10-14 . 2022-10-23 . https://web.archive.org/web/20221023231746/https://linkinghub.elsevier.com/retrieve/pii/S0022311514003468 . live .
  34. Hamaoka . T. . Nomoto . A. . Nishida . K. . Dohi . K. . Soneda . N. . December 2012 . Effects of aging temperature on G-phase precipitation and ferrite-phase decomposition in duplex stainless steel . Philosophical Magazine . en . 92 . 34 . 4354–4375 . 10.1080/14786435.2012.707340 . 2012PMag...92.4354H . 135586095 . 1478-6435 . 2022-10-14 . 2022-06-15 . https://web.archive.org/web/20220615161856/https://www.tandfonline.com/doi/abs/10.1080/14786435.2012.707340 . live .
  35. Mateo . A . Llanes . L . Anglada . M . Redjaimia . A . Metauer . G . 1997 . Characterization of the intermetallic G-phase in an AISI 329 duplex stainless steel . Journal of Materials Science . 32 . 17 . 4533–4540 . 10.1023/A:1018669217124 . 134334541 . 2022-10-14 . 2023-03-25 . https://web.archive.org/web/20230325224822/https://link.springer.com/article/10.1023/A:1018669217124 . live .
  36. Zhang . Qingdong . Singaravelu . Arun Sundar S. . Zhao . Yongfeng . Jing . Tao . Chawla . Nikhilesh . 2019-01-16 . Mechanical properties of a thermally-aged cast duplex stainless steel by nanoindentation and micropillar compression . Materials Science and Engineering: A . en . 743 . 520–528 . 10.1016/j.msea.2018.11.112 . 0921-5093 . 139168335.
  37. Lee . Ho Jung . Kong . Byeong Seo . Obulan Subramanian . Gokul . Heo . Jaewon . Jang . Changheui . Lee . Kyoung-Soo . 2018-10-01 . Evaluation of thermal aging of δ-ferrite in austenitic stainless steel weld using nanopillar compression test . Scripta Materialia . en . 155 . 32–36 . 10.1016/j.scriptamat.2018.06.016 . 1359-6462 . 139130674.
  38. Badyka . R. . Monnet . G. . Saillet . S. . Domain . C. . Pareige . C. . February 2019 . Quantification of hardening contribution of G-Phase precipitation and spinodal decomposition in aged duplex stainless steel: APT analysis and micro-hardness measurements . Journal of Nuclear Materials . en . 514 . 266–275 . 10.1016/j.jnucmat.2018.12.002 . 2019JNuM..514..266B . 105302671 . 2022-10-14 . 2022-10-23 . https://web.archive.org/web/20221023225802/https://linkinghub.elsevier.com/retrieve/pii/S0022311518312194 . live .
  39. Calcagnotto . Marion . Adachi . Yoshitaka . Ponge . Dirk . Raabe . Dierk . January 2011 . Deformation and fracture mechanisms in fine- and ultrafine-grained ferrite/martensite dual-phase steels and the effect of aging . Acta Materialia . en . 59 . 2 . 658–670 . 10.1016/j.actamat.2010.10.002 . 2011AcMat..59..658C . 2022-10-14 . 2022-06-20 . https://web.archive.org/web/20220620122943/https://linkinghub.elsevier.com/retrieve/pii/S1359645410006488 . live .
  40. Godfrey . T. J. . Smith . G. D.W. . November 1986 . The Atom Probe Analysis of a Cast Duplex Stainless Steel . live . Le Journal de Physique Colloques . 47 . C7 . C7–217–C7-222 . 10.1051/jphyscol:1986738 . 0449-1947 . 93304045 . https://web.archive.org/web/20230325224818/https://jphyscol.journaldephysique.org/articles/jphyscol/abs/1986/07/jphyscol198647C738/jphyscol198647C738.html . 2023-03-25 . 2022-10-14.
  41. May . J.E. . de Sousa . C.A.C. . Kuri . S.E. . July 2003 . Aspects of the anodic behaviour of duplex stainless steels aged for long periods at low temperatures . live . Corrosion Science . en . 45 . 7 . 1395–1403 . 10.1016/S0010-938X(02)00244-5 . 96597890 . https://web.archive.org/web/20180702084045/https://linkinghub.elsevier.com/retrieve/pii/S0010938X02002445 . 2018-07-02 . 2022-10-14.
  42. Lee . Ho Jung . Kong . Byeong Seo . Obulan Subramanian . Gokul . Heo . Jaewon . Jang . Changheui . Lee . Kyoung-Soo . October 2018 . Evaluation of thermal aging of δ-ferrite in austenitic stainless steel weld using nanopillar compression test . Scripta Materialia . en . 155 . 32–36 . 10.1016/j.scriptamat.2018.06.016 . 139130674 . 2022-10-14 . 2022-10-23 . https://web.archive.org/web/20221023225805/https://linkinghub.elsevier.com/retrieve/pii/S1359646218303701 . live .
  43. Liu . Xuebing . Zhang . Xinfang . August 2018 . An ultrafast performance regeneration of aged stainless steel by pulsed electric current . Scripta Materialia . en . 153 . 86–89 . 10.1016/j.scriptamat.2018.05.004 . 139625954 . 2022-10-14 . 2023-03-25 . https://web.archive.org/web/20230325224823/https://www.sciencedirect.com/science/article/abs/pii/S1359646218302859?via%3Dihub . live .
  44. Liu . Xuebing . Lu . Wenjun . Zhang . Xinfang . January 2020 . Reconstructing the decomposed ferrite phase to achieve toughness regeneration in a duplex stainless steel . Acta Materialia . en . 183 . 51–63 . 10.1016/j.actamat.2019.11.008 . 2020AcMat.183...51L . 210229887 . 2022-10-14 . 2022-10-24 . https://web.archive.org/web/20221024012417/https://linkinghub.elsevier.com/retrieve/pii/S1359645419307335 . live .
  45. Akita . Masayuki . Kakiuchi . Toshifumi . Uematsu . Yoshihiko . 2011 . Microstructural Changes of High-Chromium Ferritic Stainless Steel Subjected to Cyclic Loading in 475°C Embrittlement Region . Procedia Engineering . en . 10 . 100–105 . 10.1016/j.proeng.2011.04.019. free .
  46. Miller . M.K. . Stoller . R.E. . Russell . K.F. . June 1996 . Effect of neutron-irradiation on the spinodal decomposition of Fe-32% Cr model alloy . Journal of Nuclear Materials . en . 230 . 3 . 219–225 . 10.1016/0022-3115(96)80017-1 . 1996JNuM..230..219M . 2022-10-14 . 2018-06-27 . https://web.archive.org/web/20180627065845/https://linkinghub.elsevier.com/retrieve/pii/0022311596800171 . live .